Structural Adhesive

快乐飞艇玩法

Structrual Adhesive

HYLO®BOND M5101 is a toughened, two component acrylic adhesive designed for bonding a wide range of substrates.

This structural methacrylate adhesive has superior peel, shear and compressive properties. HYLO®BOND 5101 displays high toughness and can be used on gaps up to 15mm. it has a gel time of approximately 5 minutes. The adhesive has excellent fatigue and weathering resistance.

Mix ratio 10:1, cured tensile strength 16 N/mm²

快乐飞艇计划群

Pack size – 490ml

INSTRUCTIONS FOR USE

The surface to be bonded can have a great impact on the cured properties of Hylobond. Care must be taken to ensure that all traces of oil, grease and dirt are removed from the substrate. This can be done with a degreasing agent or solvent such as acetone. Abrading or etching the surface can greatly improve the properties of the bonded joint, if this is done a second degreasing process is highly recommended.

Prior to dispensing it is important to extrude the product onto a non-bonding surface to ensure that bead coming out of the nozzle is a uniform grey colour. As soon as the bead is the correct colour the product should be used immediately to prevent curing in the nozzle. Enough adhesive should be used to fill the bond gap before the parts are joined. Once the substrates are joined sufficient pressure should be applied (e.g. by clamping) to avoid dry bonding and prevent movement in the joint. These processes must be completed before the geltime expires.

The optimal application temperature is about 20°C, the geltime and cure time will be affected at temperatures much higher or lower than this. The viscosity is also affected by temperature so to ensure a consistent extrusion rate and geltime the temperature should be kept constant.

快乐飞艇人工全天计划

UNCURED MATERIALS
  Adhesive Activator
Mixing Ratio (By Weight) 9 1
Mixing Ratio (By Volume) 10 1
Specific Gravity (gml-1) 0.97 – 1.01 1.04 – 1.14
Viscosity (@22°C, cPs) 90,000 – 130,000 75,000 – 110,000
Colour Cream Black

 

MIXED MATERIAL
 Geltime (@22°C) ≈5min
Cure Time (@22°C) 14 – 18min
Gap Filling ≤15mm
Colour Grey

 

CURED MATERIAL
Tensile Strength 16 Nmm­-²
Elongation 75%
Shear Strength PVC/ABS 15 Nmm-²
Shear Strength (Aluminium) 23 Nmm-²
Shear Strength (Aluminium) 18 Nmm-²
Shear Strength (Stainless Steel/Acrylic) 22 Nmm-²